Shiva Signature Artist Oil Color - Asphaltum, 1.25 oz Tube

Pigment Information

This color contains the following pigments:

PY74-Hansa Yellow

PBk9-Ivory Black

PR101-Red Iron Oxide

Pigment Name

PY74-Hansa Yellow

Pigment Type

monoazo

Chemical Formula

C18H18N4O6

Properties

Pigment PY74 is one of the most commercially important pigments of the Hansa Yellow group, considered superior to many others in its class based on both tinting strength and lightfastness. Several PY74 grades with different particle sizes are available. Grades with finer particle size are more brilliant and transparent. Pigment PY74 ranges from reddish yellow to greenish yellow, with temperature shifts from cool to warm hues. It has high tinting strength and average to slow drying time.

Permanence

This Hansa Yellow has better lightfastness that other yellow monoazo pigments, particularly in the darker shades.

Toxicity

Hansa Yellow has no significant acute hazards, though its chronic hazards have not been well studied.

History

Hansa Yellows were first made in Germany just before WW1 from a series of synthetic dyestuffs called Pigment Yellow. They were intended to be a synthetic replacement for Cadmium Yellow.

Pigment Name

PBk9-Ivory Black

Pigment Type

charred animal bone

Chemical Name

carbon + calcium phosphate

Chemical Formula

C + Ca3(PO4)2 or C x CaPO4

Properties

Ivory Black is a cool, semi-transparent blue-black with a slight brownish undertone and average tinting strength. It mixes well with any color, and creates a range of dull greens when mixed with yellow. It has good properties for use in oil, can be slow to dry in oil form, and should never be used in underpainting or frescoing. Ivory Black is denser than Lamp Black.

Permanence

Ivory Black is very lightfast and has good permanence, though it is considered the least permanent of the major black pigments.

Toxicity

Ivory Black has no significant hazards.

History

Ivory Black is a carbon based black first named as Elephantium, and described in the 4th century BCE as produced by heating ivory scraps in clay pots to reduce the ivory or bone to charcoal. The deviation in names is because the more expensive varieties of this pigment were made by burning ivory, and the less expensive ones by burning animal bone. In the 19th century, the name Ivory Black was finally permitted to be applied to Carbon Black pigments made from bone. True Ivory Black is rare in modern times due to the protection of ivory, and the synthetic variety produced today was discovered in 1929. Bone Black is produced as an industrial pigment.

Pigment Name

PR101-Red Iron Oxide

Pigment Type

earth, synthetic

Chemical Name

iron oxides (synthetic), iron oxide, silica, alumina, lime, and magnesia or hydrated iron oxide

Chemical Formula

Fe2O2 or Fe2O3 x H2O

Properties

Red iron oxide varies in hue and transparency, depending on hydration and slight impurities. Indian Red is a slightly duller, deep brick hue with a bluish undertone. It is very dense and opaque, with excellent tinting strength and covering power. It is dependable when mixing with all other permanent pigments and yields good flesh tints when mixed with Zinc White. It is the synthetic version of PR102, which is a pigment made from earth reds, or natural red iron oxides, and the names applied to PR101 and PR102 often overlap. The synthetic red iron oxides have mostly replaced natural red iron oxides and are brighter, stronger, finer, and more permanent. Indian Red is the highest grade bluish shade. Light Red, English Red, and Venetian Red are yellowish shades. Mars Violet is a dull and subdued bluish or purplish oxide.

Permanence

Red iron oxide is very lightfast with excellent permanence.

Toxicity

Red iron oxide has no significant hazards.

History

Natural red iron oxide comes from the mineral ore hematite, called bloodstone by the ancient Greeks from the word hema, meaning blood. It is one of the oldest pigments, has been used by every major civilization, and was an important mineral for medieval alchemists. It was not widely used in artists' materials until the 17th century and was not produced in large quantities until the 18th century.