All color making is done by hand, and processes are controlled by artists. Pigments are ground in stone rather than metal rollers.
Color Swatch created using heavy application/diluted application and was applied on cold press watercolor paper (150 lb) material.
Zinc White is the coolest white, and it has a cold, clean masstone and a slightly bluish tint. It has less hiding power and is more transparent than other whites. It dries slowly and is good for painting wet into wet and for glazing and scumbling. Zinc White is neither as opaque nor as heavy as Lead White, its covering power is not as good, and it takes much longer to dry. However, it does not blacken when exposed to sulfur in the air as Lead White does. It is very valuable for making tints with other colors. Unmixed Zinc White dries to a brittle and dry paint film that may crack over the years, so it is not good for frescoing. It is more transparent in acrylic form than Titanium White and is the most commonly used white with gouache. Chinese White is a version of Zinc White appropriate for opaque watercolor techniques.
Zinc White has great permanence and lightfastness.
Zinc White is moderately toxic if ingested and slightly toxic if inhaled.
Though historians are divided on who first isolated the element zinc, they agree that it was first suggested as a white pigment in 1782. Zinc White was accepted as a watercolor in 1834 and was called Chinese White due to the popularity of oriental porcelain in Europe at the time. Ten years later, a suitable oil form was produced. By the early 20th century, it had improved to the point where it was an acceptable alternative to Flake White.
Chinese White, French White, Permanent White, Silver White, Snow White, Zinc Oxide.
Pigment PY74 is one of the most commercially important pigments of the Hansa Yellow group, considered superior to many others in its class based on both tinting strength and lightfastness. Several PY74 grades with different particle sizes are available. Grades with finer particle size are more brilliant and transparent. Pigment PY74 ranges from reddish yellow to greenish yellow, with temperature shifts from cool to warm hues. It has high tinting strength and average to slow drying time.
This Hansa Yellow has better lightfastness that other yellow monoazo pigments, particularly in the darker shades.
Hansa Yellow has no significant acute hazards, though its chronic hazards have not been well studied.
Hansa Yellows were first made in Germany just before WW1 from a series of synthetic dyestuffs called Pigment Yellow. They were intended to be a synthetic replacement for Cadmium Yellow.
Arylide, Arylide Yellow, Azo, Brilliant Yellow, Monoazo, Monolite Yellow, Permanent Yellow.
iron(III)-oxide, partly hydrated
Brown Ochre provides artists with earthtones from cream to brown and is a dull, dark variety of Yellow Ochre. Its transparency varies widely from opaque shades to more transparent ones, which are valued for their use as glazes. It has good hiding power, produces a quick drying paint, and can be safely mixed with other pigments. The highest quality Brown Ochre comes from Cyprus, where it is yellow in its raw form and is roasted to get the deeper brown-red varieties that result when water is removed. (See Yellow Ochre, PY42/43.)
Brown Ochre has excellent permanence.
Brown Ochre is non-toxic.
Ochre comes from the Greek word ochros, meaning pale yellow. It has been used since prehistoric times, and evidence of its use has been found in some of the earliest known cave paintings in Lascaux, France. It has also been called Goethite, after the German philosopher and mineralogist Johann Wolfgang von Goethe (1749-1832).
Goethite, Yellow Ochre.
complex silicate of sodium and aluminum with sulfur
Na8-10Al6Si6O24S2-4 or Na6-8Al6Si6O24S2-4
Ultramarine is the standard warm blue, a brilliant blue pigment that has the most purple and least green in its undertone. It has a moderate to high tinting strength and a beautiful transparency. Synthetic Ultramarine is not as vivid a blue as natural Ultramarine. Ultramarine dries slowly in oil and tends to produce clean, though granular, washes in watercolor. French Ultramarine mixes well with Alizarin colors in oil and watercolor form to create a range of purples and violets. It can dull when mixed with white in acrylic form, but mixes well with other colors. The shade varies based on manufacturer. Considered a great color for glazes, it is not suitable for frescoing.
Ultramarine has excellent permanence, although synthetic Ultramarine is not as permanent as natural Ultramarine. It may discolor if exposed to acid because of its sulfuric content.
Ultramarine has no significant hazards.
The name for this pigment comes from the Middle Latin ultra, meaning beyond, and mare, meaning sea, because it was imported from Asia to Europe by sea. It is a prominent component of lapis lazuli and was used on Asian temples starting in the 6th century. It was one of the most expensive pigments in 16th century Europe, worth twice its weight in gold, and so was used sparingly and when commissions were larger. Ultramarine is currently imitated by a process invented in France in 1826 by Jean Baptiste Guimet, making blue affordable to artists and extending the range of colors on their palettes.
Artificial Ultramarine, French Blue, French Ultramarine, Gmelin's Blue, Guimet’s Blue, Permanent Blue, Royal Blue, Synthetic Ultramarine. New Blue describes particular shades of Ultramarine. Armenian Blue and Lazuline Blue are names for genuine Lapiz Ultramarine. Sky Blue is a pale tone of Ultramarine.